5% Bare (2.4mm)
Stay-Silv® 5 Phos-Copper Brazing Alloy
• 2.4mm x 503mm x 1kg Pack
• Round Rod
• Medium-range silver brazing alloy for copper-to-copper applications
• More ductile than Harris® 0 or Stay-Silv® 2
• A frequent choice for brazing copper as it is "self-fluxing"
• When heated quickly to its liquidus, allows penetration into tight clearance connections
• With slower heating, the alloy melting range allows the operator to fill loose connections
• Use Stay-Silv® white flux to braze low-zinc brass
• Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including Stay-Silv® 5, should not be used if the braze is exposed to sulfur or sulfur compounds in service
• Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
• The phosphorus content promotes formation of a low ductility intermetallic with the base metal