Harris® 0 Phos-Copper Brazing Alloy
• 2.4mm x 508mm x 11.34kg box
• Economical choice for copper brazing
• Copper is self-fluxing, so no manual flux application is required
• Alloy flows quickly at brazing temperature requiring close joint tolerance, less than 0.005 in. (0.13 mm)
• Primarily used in manual brazing applications
• Suitable for brazing brass
• When brazing brass, operators should avoid over heating and use Stay Silv® white brazing flux
• Not recommended for brazing steel or other ferrous base metals
• Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including Harris® 0, should not be used if the braze is exposed to sulfur or sulfur compounds in service
• Recommended joint clearance of 0.002 in. - 0.005 in. (0.05 mm - 0.13 mm)